Volkswagen Touran Service Manual: Two-Part HS Clear Coat

Definition:
Two-Part HS Clear Coat -L2K 769 500 A5-
Edition 10/2012
Product Description
Two-part HS clear coat is a VOC compliant, high-quality high solid clear coat.
Properties:
Easy to process
Variable uses for two-part HS and two-part VHS hardeners
Good spreading properties
Brilliant surface finish
Application Instructions
Base Surface
Suitable preliminary coatings:
Water-based base paints
Suitable pre-treatment materials:
Dependent on the object and base surface, according to our structure recommendations.
   
Processing with Two-Part HS Hardeners
Mixture ratio:
  2:1 by volume with:
Two-Part HS Hardener -LHA 009 041 A3-
Two-Part HS Hardener, Short -LHA 021 004 A3-
Two-Part HS Hardener, Extra Short -LHA 009 046 A2-
Two-Part HS Hardener, Long -LHA 009 047 A3-
Two-Part HS Hardener, Extra Long -LHA 009 048 A3-
See technical application information two-part HS hardener. Refer to → Chapter "Two-Part HS Hardener".
  Two-Part HS Clear Coat
Processing time/pot life:
  Ready for spraying in 90 minutes at +20 C (68 F)
  Two-Part HS Clear Coat
Application type "coat"
  Two-Part HS Clear Coat
  Processing viscosity at +20 C (68 F) material temperature is the mixing viscosity for "Compliant" and "HVLP".
  Two-Part HS Clear Coat
  Set spray nozzle (see manufacturer's information): "Compliant" 1.3 to 1.4 mm.
  Set spray nozzle (see manufacturer's information): "HVLP" 1.3 to 1.5 mm.
  Set spray pressure (see manufacturer's information): "Compliant" to 2.0 to 2.5 bar.
  Set atomizing pressure (see manufacturer's information): "HVLP" 0.7 bar.
  Two-Part HS Clear Coat
  The recommended dry layer thickness is between 50 and 60 mm.
  Two-Part HS Clear Coat
Processing with Two-Part VHS Hardeners
Mixture ratio:
  3:1 by volume with:
Two-Part VHS Hardener -LHA 009 051 A2-/-LVM 009 051 A5-
Two-Part VHS Hardener, Short -LHA 009 050 A2-
Two-Part VHS Hardener, Long -LHA 009 052 A2-/-LHA 009 052 A3-
Two-Part VHS Hardener, Extra Long -LHA 009 053 A2-
See technical application information for the two-part VHS hardener. Refer to → Chapter "Two-Part VHS Hardener and Two-Part VHS Performance Hardener".
Thinner:
Two-Part Thinner, Special -LVM 009 200 A2-/-LVM 009 200 A5-
  Two-Part HS Clear Coat
Processing time/pot life:
  Ready to spray in 60 to 90 minutes at +20 C (68 F)
  Two-Part HS Clear Coat
Application type "coat"
  Two-Part HS Clear Coat
  Processing viscosity at +20 C (68 F) material temperature is the mixing viscosity for "Compliant" and "HVLP".
  Two-Part HS Clear Coat
  Add 12.5 to 15 % Two-Part Thinner, Special -LVM 009 200 A2-/-LVM 009 200 A5-.
  Two-Part HS Clear Coat
  Set spray nozzle (see manufacturer's information): "Compliant" 1.3 to 1.4 mm.
  Set spray nozzle (see manufacturer's information): "HVLP" 1.3 to 1.5 mm.
  Set spray pressure (see manufacturer's information): "Compliant" to 2.0 to 2.5 bar.
  Set atomizing pressure (see manufacturer's information): "HVLP" 0.7 bar.
  Two-Part HS Clear Coat
  1.5 spray applications are required to get the recommended dry layer thickness of between 50 and 60 mm.
  Two-Part HS Clear Coat
Drying
Air dry at +20 C (68 F) room temperature:
Dust dry after 40 to 50 minutes
Ready for assembly after 4 to 6 hours
Dry overnight
  Two-Part HS Clear Coat
The drying time with forced drying is at least 5 to 10 minutes.
  Two-Part HS Clear Coat
Forced dry at +60 C (140 F) object temperature for 30 to 40 minutes
  Two-Part HS Clear Coat
Final drying time for IR drying is at least 5 minutes.
  Two-Part HS Clear Coat
IR dry with a short-wave heater for 10 to 15 minutes and with a medium-wave heater for 15 to 20 minutes
  Two-Part HS Clear Coat
Special Instructions
Elastification for rigid and semi-rigid plastics:
The base material must first be mixed with 15 % Elastic Additive -ALZ 011 001-.
Mixture with two-part HS hardeners, 2:1
Mixture with two-part VHS hardeners, 3:1 with 15 % thinner (drying period is lengthened).
  Two-Part HS Clear Coat
Personal Protective Equipment:
Note the safety data sheets
Wear the personal protective equipment during application
Characteristics
  Two-Part HS Clear Coat
Flashpoint: above +23 C (73.4 F)
VOC value: 2004/42/IIB(d)(420)420 The EU limit for this product (product category IIB.b) in ready-to-use form is a maximum of 420 g/L volatile organic compounds. The VOC-value of this product in ready-to-use form is a maximum of 420 g/L.
 
     
Storage
The guaranteed shelf life of Two-Part HS Clear Coat -L2K 769 500 A5- is 48 months from date of manufacture. Use no later than the date indicated on the label and store in original container at +20 C (68 F).
  Two-Part HS Clear Coat
Clear Coats
...

Two-Part MS Matte Clear Coat
Definition: Two-Part MS Matt Clear Coat -L2K 769 020 A2- Edition 08/2013 Product Description ...

Other materials:

Volkswagen Touran Service Manual. Light Alloy Wheels, Care and Maintenance
To maintain the decorative appearance of light alloy wheels for a long time, regular care is necessary. In particular, road salt and dust from brake abrasion must be thoroughly washed off every two weeks. Otherwise, the paint of the ligh ...

Volkswagen Touran Service Manual. Wire Break with Dual Repair Point
Repair point with intermediate wire section   Free up wire intended for repair at two points (approximately 20 cm to both sides of respective repair points).   If required, remove wiring harness wrapping ...

© 2016-2024 Copyright www.vwtouran.net | 0.0166